Naphthlene Sulfonate - Based Super Plasticiser
DISPERSING AGENT NOF TS CS (CALCIUM SALT)
Base Napthlene Napthlene Napthlene
Calcium CA Nil Nil .60%
PH 10% Solwater 7.25 + 1% 7.25 + 1% 7.25 + 1%
Sulphate Content <7% <3% Nil
Ash Content <35% <35% <29%
Appearce Fine Powder Fine Powder Fine Powder
Colour Off-White Off-White Off-White
Density 600-700 KG/M Cube 600-700 KG/M Cube 600-700 KG/M Cube
Solubility Solubility in water Solubility in water Solubility in water
Ch. Composition Napthalene Sulfonate formaldehyde Sodium Salt Napthalene Sulfonate formaldehyde Sodium Salt Napthalene Sulfonate formaldehyde Sodium Salt
Cas No. 9084-06-4 9084-06-4 9084-06-4
Moisture <5% <5% <5%

Applications :

Construction Chemical Super Plasticizers.
Cement Water Reducer & rapid setting /Cement grinding
Admix Super-Plasticizer increases compressive strength & workability to concrete
Gypsum, Clay, Ceramics Water Reducer allows to prepare a higher solids slurries, increase production.
Oil Field Viscosity reducer of cement slurry used in cementing casing in wells.

SNF 40% LIQUID (NAPHTHALENE SULFONATE FROM DEHYDE CONDENSED)

Appearance Brown
Total Solid Content at 105_+2ºC 40%-42%
Specific Gravity 1.18-1.20
Ph of 10% Sol/Wt 7.5(+1%)
Sulphated ash at 750ºC on LPDR Bases <35%
Water Insoluble Nil
Slump Characteristics With control slump of 50 mm with SNF 40%@1% Dosage, Collapsible Slump can be achieved for 15-30 Minutes. Depending upon Weather & Concrete Conditions. Self - Life have SNF-40% Liquid best before 12 Mths.
Water Reduction Up to 30%
Air Entrainment 1% Additional Air
Strength High Early Strength
Flowability Floable Concrete with High Strength
Chlorides Absent
Free Sulftecontent 7.5% Max
Special Instructions To be Shaken / Stirred before use
Packing 250 KG Barrels or Tanker Loads